聚丙烯增强纱管料

聚丙烯增强纱管料特征：玻纤增强
聚丙烯增强纱管料用途：纱管专用料
密度 ASTM D-792 --- 1.38 g/cm3
线性成型收缩率 ASTM D-955 --- 0.26 %
熔体流动速率 ASTM D-1238 230°C/2.16kg 3 g/10min
拉伸强度 ASTM D-638 --- 120 MPa
断裂伸长率 ASTM D-638 --- 2 %
屈服弯曲强度 ASTM D-790 6.4mm 165 MPa
弯曲模量 ASTM D-790 6.4mm 9800 MPa
悬臂梁缺口冲击强度 ASTM D-256 干湿不断裂 18 KJ/m2
烘干温度/时间 --- --- 80/4-6 ℃/hr
注塑成型温度范围 --- --- 170-230 ℃
注塑成型参考模温 --- --- 70-80 ℃
热变形温度 ASTM D-648 --- 168 ℃